Connection between Mechanical Relaxation and Equilibration Kinetics in a High-Entropy Metallic Glass.

The slow transition from an out-of-equilibrium glass towards a supercooled liquid is a complex relaxation phenomenon. In this Letter, we study the correlation between mechanical relaxation and equilibration kinetics in a Pd_{20}Pt_{20}Cu_{20}Ni_{20}P_{20} high-entropy metallic glass. The evolution of stress relaxation with aging time was obtained with an unprecedented detail, allowing us to pinpoint new interesting features. The long structural relaxation towards equilibrium contains a wide distribution of activation energies, instead of being just associated to the ß relaxation as commonly accepted. The stress relaxation time can be correlated with the equilibration rate and we observe a decrease of microstructural heterogeneity which contrasts with an increase of dynamic heterogeneity. These results significantly enhance our insight of the interplay between relaxation dynamics and thermodynamics in metallic glasses.

Influence of nanosecond laser surface patterning on dental 3Y-TZP: Effects on the topography, hydrothermal degradation and cell response.

OBJECTIVES: Laser surface micropatterning of dental-grade zirconia (3Y-TZP) was explored with the objective of providing defined linear patterns capable of guiding bone-cell response. METHODS: A nanosecond (ns-) laser was employed to fabricate microgrooves on the surface of 3Y-TZP discs, yielding three different groove periodicities (i.e., 30, 50 and 100 µm). The resulting topography and surface damage were characterized by confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM). X-Ray diffraction (XRD) and Raman spectroscopy techniques were employed to assess the hydrothermal degradation resistance of the modified topographies. Preliminary biological studies were conducted to evaluate adhesion (6 h) of human mesenchymal stem cells (hMSC) to the patterns in terms of cell number and morphology. Finally, Staphylococcus aureus adhesion (4 h) to the microgrooves was investigated. RESULTS: The surface analysis showed grooves of approximately 1.8 µm height that exhibited surface damage in the form of pile-up at the edge of the microgrooves, microcracks and cavities. Accelerated aging tests revealed a slight decrease of the hydrothermal degradation resistance after laser patterning, and the Raman mapping showed the presence of monoclinic phase heterogeneously distributed along the patterned surfaces. An increase of the hMSC area was identified on all the microgrooved surfaces, although only the 50 µm periodicity, which is closer to the cell size, significantly favored cell elongation and alignment along the grooves. A decrease in Staphylococcus aureus adhesion was observed on the investigated micropatterns. SIGNIFICANCE: The study suggests that linear microgrooves of 50 µm periodicity may help in promoting hMSC adhesion and alignment, while reducing bacterial cell attachment.

Mechanical reliability of dental grade zirconia after laser patterning.

The aim of this work is to test the mechanical properties of dental zirconia surfaces patterned with Nd:YAG laser interference (λ = 532 nm and 10 ns pulse). The laser treatment produces an alteration of the topography, engraving a periodic striped pattern. Laser-material interaction results mainly in thermal effects producing microcracking, phase transformation and texturization. The role of such microstructural modifications and collateral damage on the integrity and mechanical performances has been assessed. Laser patterned discs of zirconia doped with 3% mol yttria (3Y-TZP) have been tested before and after a thermal treatment to anneal residual stresses and revert phase transformation. Both groups of samples behave in a similar manner, excluding residual stresses and phase transformation from the origin of properties modification. Result show that laser patterning induces a minor decrease in mechanical properties and surface integrity of 3Y-TZP surfaces. The biaxial strength decreases as a consequence of the damage induced by laser patterning. Fractographic observations identify preexisting defects enlarged by local laser interaction as the fracture origins. The Hardness and Young modulus of treated surfaces tested with nanoindentation also decrease slightly after laser treatment and this may be attributed to laser-induced microcracking.

Contact fatigue of veneer feldspathic porcelain on dental zirconia.

OBJECTIVES: To understand the resistance to cyclic and static contact loading of feldspathic porcelain on dental zirconia (3Y-TZP), in order to understand the partial failure of porcelain (chipping or cracking). METHODS: Hertzian contact techniques were used to evaluate the appearance of damage as a ring crack in terms of applied load and number of cycles in air and simulated saliva. RESULTS: Static contact loading showed the presence of stress corrosion cracking in the porcelain; the environmental crack growth in air was determined from the results of time to damage under static load. There was also a contribution of fatigue effects due to the interactions of the crack with the microstructure. From the obtained results, a time to failure was estimated depending on the material counterpart. Cracking can occur on porcelain coatings if the contact counterpart is teeth or porcelain in a time interval of a few years, consistent with clinical studies. SIGNIFICANCE: Contact loading, particularly against teeth or other ceramic materials can be a significant cause of failure and chipping of feldspathic porcelain on zirconia, especially if the patient suffers from bruxism. Protection, by e.g. a guard, against repetitive contact against the porcelain can increase the lifetime of the veneer.